Fused Cast Skid Rail Block TY-GM5 TY-GM20
Apparent Prosity: 3.55%
True density: 350g/cm3
Cold Crushing Strength: 120Mpa
Hot Crushing Strength 1300℃: /
Exudation temperature of Glass phase℃: 0.9
Thermal conductivity 1250 ℃: 9.2(W/MK)
- SHARE:
Feature
▶ Descriptions:
Fused cast skid rail blocks TY-GM5 TY-GM20 produced at sunrise are of various types including steel discharging platform brick,skid rail block and iron discharging tank blocks.This series block features great strength,good wear and fused slag corrosion resistance as well as long service life(one to two years). Compared to fused cast AZS and zircon mullite bricks,fused cast skid rail block can reduce maintenance cost and increase furnace efficiency.
▶ Specification and application:
◆ Mainly made from Al2O3 and ZrO2, it has excellent performance in fire resistance degree, softening deformation temperature,flexural strength,curving temperature,stability and fused slag corrosion,etc. Widely used for steel reheating stove skid rail and steel discharging platform,slot and other consumable parts in industrial furnaces.
◆ High abrasion and temperature resistance, ideal for large billet,large friction parts and steel discharging parts in reheating stoves.
◆ Gliding rail bricks in steel pusher metallurgical furnaces, the tapping platform (tapping spout) style walking beam furnaces, and also as the interior for incinerators.
Technical Data
| Item | Behaviors TY-GM20 | |||
| Special | Typical | |||
| Chemical Composition (%) | Al2O3 | 71-74 | 73 | |
| ZrO2 | 19-22 | 20.5 | ||
| SiO2 | 5-8 | 6.0 | ||
| Fe2O3 | ≤0.5 | 0.3 | ||
| Na2O | ≤1.0 | 0.5 | ||
| CaO | ≤0.5 | 0.5 | ||
| Apparent Prosity (%) | 5-8 | <8 | ||
| True density (g/cm3) | ≥3.0 | 3.55 | ||
| Cold Crushing Strength (Mpa) | ≥250 | 350 | ||
| Hot Crushing Strength 1300℃ (Mpa) | 120 | |||
| Exudation temperature of Glass phase℃ | ||||
| Line Expansion 1150℃ (%) | 0.9 | |||
| Thermal conductivity 1250℃ (W/MK) | 9.2 | |||
| Bulk Density (g/cm3) | PT(RN) | ≥3.0 | ||
| WS(VF) | ≥3.2 | |||
| Crystallographic analysis (%) | Corundum | 71 | ||
| Mullite | - | |||
| Glass Phase | 9 | |||
| Baddeleyite | 20 | |||